SO GIANT OIL SEAL INDUSTRIAL CO., LTD. TEST REPORT MATERIAL: KF10173A Press Cure Post Cure Date: 10/15/02 Sheet: 10 min 175 ℃ Sheet: 24 hrs 235 ℃ Button: 10 min 175 ℃ Button: 24 hrs 235 ℃	ATF Water Resistance: 150 ℃ * 70 hrs Hardness Change Tensile Strength Change Elongation Change Volume Change
	EO ASTM #1 Oil: 150 ℃ * 70 hrs Hardness Change － 2 Tensile Strength Change ＋17 Elongation Change －14 Volume Change 0
Spec: Original Properties: no post Spec. Hardness (Shore A) 74 76 Tensile Strength ( Kg/c㎡) 90 119 Elongation, ％ 355 274 Tear Resistance ( Kg/㎝) 36 39 Modulus at 100 ％ 32 44 Modulus at 200 ％ 56 82 Modulus at 300 ％ 70 Specific Gravity 2.172
	EO ASTM #3 Oil: 150 ℃ * 70 hrs Hardness Change － 3 Tensile Strength Change ＋ 5 Elongation Change －13 Volume Change ＋ 2.2
	EO ATF Oil: ℃ * hr Hardness Change － 3 Tensile Strength Change ＋ 2 Elongation Change －22 Volume Change ＋ 2.4
A Heat Resistance: 250℃ * 70 hrs Hardness Change 0 Tensile Strength Change ＋ 6 Elongation Change － 7 Volume Change (Weight Lose %) － 3.2	EF Fuel C Resistance: 23 ℃ * 70 hrs Hardness Change － 5 Tensile Strength Change －19 Elongation Change －17 Volume Change ＋ 5.6
A Heat Resistance: 275 ℃ * 70 hrs Hardness Change ＋ 2 Tensile Strength Change －22 Elongation Change － 3 Volume Change － 3.4	EF Fuel B Resistance: 23 ℃ * 70 hrs Hardness Change － 4 Tensile Strength Change －12 Elongation Change － 7 Volume Change ＋ 1.1
B Compression Set: 200 ℃ * 70 hrs 38.7 B Compression Set: 200 ℃ * 22 hrs 25.4 B Compression Set: 175 ℃ * 22 hrs 15.5	EF Fuel Resistance: 23 ℃ * 70 hrs Hardness Change Tensile Strength Change Elongation Change Volume Change
C 12 50 pphm * 40 ℃ * 70 hrs C pphm * ℃ * hr
	F Low Temperature: ℃* min