SO GIANT OIL SEAL INDUSTRIAL CO., LTD. TEST REPORT MATERIAL：
NB00170A
Press
Cure
Post Cure Date: Sheet: 5 min 170 ℃
Sheet: 60 min
120 ℃ Button: 10 min 170 ℃
Button:
60 min 120 ℃ |
EA
14 Water Resistance : 100 ℃
＊
70 hrs Hardness Change
－ 1 Tensile Strength
Change
＋ 2 Elongation Change － 9 Volume Change
＋ 6.5 |
|
|
EO
14 ASTM # 1 Oil :
100 ℃ ＊
70 hrs Hardness Change
＋
5 Tensile Strength
Change
＋ 4 Elongation Change
－ 14 Volume Change
－ 5.8 |
||
|
Spec: ASTM
D2000M2BG714B14EA14EO14EO34EF11EF21 |
||
|
Original Properties:
no post Spec. Hardness
(Shore A)
73 Tensile Strength
(psi)
2343 Elongation, ％
298 Tear resistance (㎏-㎝)
63 Modulus at 100 ％
59 Modulus at 200 ％
120 Modulus at 300 ％
158 Specific
Gravity
1.245 |
EO
34 ASTM # 903 Oil 100 ℃
＊
70 hrs Hardness Change
－ 5 Tensile Strength
Change
＋ 2 Elongation Change
－
16 Volume Change
＋ 7.5 |
|
|
EO Gasline
Oil : 23 ℃
＊
70 hrs Hardness Change
－ 15 Tensile Strength
Change
－ 30 Elongation Change
－ 35 Volume Change
＋ 17.9 |
||
|
A14 Heat Resistance: 100 ℃
*＊
70 hrs Hardness
Change
＋ 5 Tensile
Strength Change
＋ 4 Elongation
Change
－18 Volume
Change
－ 2.4 |
EF 95 No.Pb
Oil : 23 ℃
＊
70 hrs Hardness Change
－ 16 Tensile Strength
Change
－
25 Elongation Change
－ 30 Volume Change
＋ 20.8 |
|
|
EF
11 Fuel A Resistance : 23℃
＊
70 hrs Hardness Change
－ 1 Tensile Strength
Change
＋ 7 Elongation Change
－14 Volume Change
＋
2.8 |
||
|
A14
Heat Resistance: 100 ℃
*＊
70 hrs Hardness Change
Tensile Strength Change Elongation Change Volume Change |
||
|
EA
21 Fuel B Resistance : 23 ℃
＊
70 hrs Hardness Change －14 Tensile Strength
Change
－20 Elongation Change
－19 Volume Change
＋20.4 |
||
|
B
14 Compression Set: 100 ℃
＊ 22 hrs
13.2 B Compression Set: 100 ℃ ＊ 70 hrs 18.4 B Compression Set: 125 ℃ ＊ 70 hrs 27.6 |
||
|
F16
Low Temperature －33 ℃ ＊ 3 min.
PASS |